Nickel doped zinc selenide (Ni:ZnSe) thin films by simple chemical bath deposition (CBD) method in an aqueous alkaline medium the bath temperature at 70°C. The doped Ni2+ ions different concentrations varied from 1 to 7 mol % and also these deposited thin films were annealed in an open atmosphere with various temperatures at 400, 500 and 600°C respectively. XRD, UV-vis spectrum and PL spectroscopes. XRD results revealed that the Ni:ZnSe thin films are showed mixture of cubic and hexagonal systems along with some NiO and ZnO phase. The PL studies confirmed that the Ni2+ ions doped ZnSe thin films were showed a prominent emission peak centre at 405 nm and a weak emission peak centre at 411 nm.